We report the current limiting properties of superconducting fault current limiters (SFCL). Our SFCL was patterned in a spiral type on a YB $a_2$C $u_3$$O_{7-x}$(YBCO) film deposited using rf sputtering techniques and was coated with a gold shunt layer in order to disperse the heat generated at hot spots in the YBCO film. Current increased up to 13.5 $A_{peak}$ at 60 Hz for the voltage of 13 $V_{peak}$, which is the minimum quench point, and increased up to 17.6 $A_{peak}$ at 60 Hz fo the voltage fo 141.4 $V_{peak}$. The quench completion time was 5 msec at 13 $V_{peak}$ and 4 msec at 141. $V_{peak}$ respectively. we think that this architecture using spiral-type SFCL can be useful for the protection of the power delivery systems from fault currents.s. currents.s.