The chemical-mechanical polishing process was carried out for 2"-dia. sapphire wafer grown by horizontalBridgman method on the urethane lapping pad with the silica sol. The polished wafer shows the full-width at halfmaximum of 200~400 arcsec in double-crystal X-ray diffraction, indicating that the slicing, grinding and lapping processes before the polishing process affected the crystalline structural property of the wafer surface by the mechanical residual stress. For the inclusion of surface treatments after chemical-mechanical polishing such as the thermal annealing at the temperature of $1,200^{circ}C$for 4 hrs. and chemical etching, the crystalline quality was sigdicantly enhanced with the reduced full-width at half maximum up to 8.3 arcsec.arcsec.