Crystal structure of PbBi$_2$Nb$_2$$O_{9}$ and $Sr_{1.2}$$Bi_{1.8}$Ta$_2$$O_{9}$ were determined by Rietveld method using neutron diffraction data in the temperature range of 300 K~1273K. Phase transition temperature were measured from the dielectric permittivitytemperature curve. The PbBi$_2$Nb$_2$$O_{9}$ showed a phase transition at about 810 K. In the Sr-excess compound $Sr_{1.2}$$Bi_{1.8}$Ta$_2$$O_{9}$ the phase transition was suppressed down to room temperature. Several structural models were tested by the Rietiveld refinement. Based on the `R` values and the structural parameters, the B2cb model is judged to be the most feasible one for the high temperature phase at above 810 K of the PbBi$_2$Nb$_2$$O_{9}$. The $Sr_{1.2}$$Bi_{1.8}$Ta$_2$$O_{9}$ sample was refined to show the most reliable results by the Am2m model.sults by the Am2m model.