The objective of the present study was to investigate the characteristics of the friction and wear according to the amount of ion-irradiation for the carbon fiber reinforced plastic(CFRP). Unidirectional carbon fiber reinforced composites were fabricated with epoxy resin as a matrix and carbon fiber as a reinforcement, and its surface was modified by the ion-assisted reaction. When the amount of ion-irradiation was $1{ imes}10^{16}$ ions/$cm^2$, the friction coefficients of composites were about 0.1 and the wear mode was stable, whereas, the friction coefficient of non-treatment composites were about 0.16 and the wear mode was very unstable. But if the amount of ion-irradiation was $5{ imes}10^{16}$ ions/$cm^2$, the friction coefficients were higher rather than that of $1{ imes}10^{16}$ ions/$cm^2$. Consequently, the amount of ion-irradiation was not in proportion to the friction coefficients, and it was conformed that the optimal conditions would exist between broth of them.