Due to increase of air pollution substance, such as $SO_2$,$SO_3$, H2S ,CO, HCI, $Cl_2$ and so on, the operating environment of mechanical equipment and facilities like generating plants, ships, metal structure etc., are acidified and corroded. In these environments, the crevice corrosion of marine facilities frequently occurs at crevice like jointed bolt, gasket or sealant, riveted plates, contact of metal with non-metallic solids etc. Therefore, this paper was studied on the crevice corrosion behavior of mild steel(SS 400) in marine environment. In a variety of NaCl solutions, the aspect of he .crevice corrosion and polarization behavior under the crevice corrosion was investigated. The main results obtained are as follows: 1) Under crevice corrosion, the open circuit potential become less treble as the concentration of NaCl solution increased. 2) The corrosion current density of mild steel was high drained as the concentration of NaCl solution increased by 3.5%, but in the concentration increased over 3.5%, the corrosion current density was low drained. 3) The crevice corrosion is more sensitive to the synergy effect of dissolved oxygen and NaCl.