The reaction stability of nickel with side-wall materials of SiO$_2$ and Si$_3$N$_4$ on p-type 4"(100) Si substrate were investigated. Ni on 1300 $AA$ thick SiO$_2$ and 500 $AA$ - thick Si$_3$N$_4$ were deposited. Then the samples were annealed at 400, 500, 750 and 100$0^{circ}C$ for 30min, and the residual Ni layer was removed by a wet process. The interface reaction stability was probed by AES depth Profiling. No reaction was observed at the Ni/SiO$_2$ and Ni/Si$_3$N$_4$, interfaces at 400 and 50$0^{circ}C$. At 75$0^{circ}C$, no reaction occurred at Ni/SiO$_2$ interface, while $NiO_x$ and Si$_3$N$_4$ interdiffused at Ni/Si$_3$N$_4$ interface. At 100$0^{circ}C$, Ni layers on SiO$_2$ and Si$_3$N$_4$ oxidized into $NiO_x$ and then $NiO_x$ interacted with side-wall materials. Once $NiO_x$ was formed, it was not removed in wet etching process and easily diffused into sidewall materials, which could lead to bridge effect of gate-source/drain.