The mutually reactive copolymers poly[(vinylbenzyl chloride)-co-(n-butyl acrylate)-co-(2-hydroxyethyl methacrylate)] and poly[(4-vinylpyridine)-co-(n-butyl acrylate)-co-(2-hydroxyethyl methacrylate)] were synthesized for the humidity sensitive material by forming simultaneous quaternization. The humidity sensor showed an average resistance of 8.6 M$Omega$, 310 k$Omega$ and 12 k$Omega$ at 30%RH, 60%RH and 90%RH, respectively. The hysteresis and temperature coefficient were $pm$3%RH and -0.37~-0.40%RH/$^{circ}C$. The introduction of n-BA and HEMA increased the resistance of the humidity sensor however it enhanced the adherence to the alumina substrate. The response time was 54 seconds changing from 33%RH to 85%RH and the difference of resistance was +0.2%RH after soaking in water for 2 hr.