The leakage current behaviors of PLZT capacitors with top electrodes of Pt, Ir, and $IrO_2$ are investigated before and after hydrogen forming gas anneal. The P-E hysteresis and fatigue properties of Pt/PLZT/Pt capacitors are almost recovered after recovery anneal in $O_2$ ambient. The leakage current mechanisms of PLZT capacitors with Pt and $IrO_2$ top electrodes are consistent with space-charge influenced injection model showing the strong time dependence irrespective of annealing conditions. On the other hand, the leakage current behavior of Ir/PLZT/Pt capacitor shows steady state independent of time because IrPb, conducting phase, formed at interface between Ir top and PLZT is a high conduction path. Teh leakage current mechanism of Ir/PLZT/Pt capacitor is consistent with Schottky barrier model.