Composition effects on microstructure and metallizing properties of the alumina sintered body were evaluated to develop the metallized alumina tubes having superior properties for electronic devices. SEM observation revealed that resultant micrographs and fractographs were varied with composition chance of additives and $SiO_2$-rich specimens showed better microstructural characteristics with uniform distribution of fine and round particles than other CaO-rich or MgO-rich ones. The resultant interfacial microstructure of the $SiO_2$-rich metallized alumina tubes also showed good metallizing properties with no defects between layers and uniform thickness of metallizing layer.