Effects of coating treatment of metallic Cu film on SiC for Al/SiC composite were studied. The Copper was deposited on SiC by electroless plating method. Al/sic composite was fabricated at temperature range of $670^{circ}C$ to 90$0^{circ}C$ under vacuum atmosphere. The wetting behavior of Al/SiC composite were analysed by SEM and XRD. The coating treatment on SiC improved wettability of Al melt on SiC considerably comparing to the non coated SiC. This improved wettability seems strongly concerned to the increase of chemical reactivity between coated layer and Al matrix. The improvement of wettability of Al melt on the Cu coated SiC was closely related to in the initial stage of reaction. The metallic film played an important role in reducing the interfacial free energy and breaking down the aluminum oxide film through the reaction with Al melt. The wetting behavior of the as-received SiC with Al melt was not uniform, indicated by the contact angles from less than $97^{circ}$to more than $97^{circ}$.