The effect of S content in welding wires on spattering characteristics and droplet transfer phenomena was studied. In MAG welding using 80%Ar-$20%CO_2$ shielding gas, spattering characteristics and droplet transfer phenomena were varied with S content of wire. Sulfur addition in wire reduced surface tension of droplet and weld pool, and made arc more stable in MAG welding. With increasing S content, the spattering ratio and the ratio of large size spatter ($d{geq}1.0mm$) were reduced in short circuit transfer mode. In spray transfer mode, spattering ratio, however was increased when sulfur was added more than 0.020wt.% because surface tension of droplets and weld pool was reduced too much even though arc stability was improved.