In this paper, hermetic sealing technology was studied for wafer level packaging of the RF-MEMS devices. With the flip-chip bonding method. this non-conductive B-stage epoxy sealing will be profit to the MEMS device sealing. It will be particularly profit to the RF-MEMS device sealing. B-stage epoxy can be cured by 2-step and hermetic sealing can be obtained. After defining 500 $mu extrm{m}$-width seal-lines on the glass cap substrate by screen printing, it was pre-baked at $90^{circ}C$ for about 30 minutes. It was, then, aligned and bonded with device substrate followed by post-baked at $175^{circ}C$ for about 30 minutes. By using this 2-step baking characteristic, the width and the height of the seal-line could be maintained during the sealing process. The height of the seal-line was controlled within $pm$0.6 $mu extrm{m}$ in the 4 inches wafer and the bonding strength was measured to about 20MPa by pull test. The leak rate, that is sealing characteristic of the B-stage epoxy, was about $10^{-7}$ cc/sec from the leak test.