Spin dependent tunneling (SDT) junction devices of Ta/NiFe/Ta/NiFe/FeMn/NiFe/AlOx/CoFe/NiFe/Al with in-situ naturally oxidized Al barrier were fabricated using ion beam deposition and dc sputtering in UHV chamber of 10$^{-9}$ Torr. The maximum tunneling magnetoresistance (TMR) and the product resistance by junction (R$_{j}$ A) are 16-17% and 50-60 $Omega$${mu}{ extrm}{m}$$^2$, respectively. The values of TMR and (R$_{j}$ A) with field annealing were slightly increased. The TMR and (R$_{j}$ A) dependence versus the junction area size was observed. These results were explained by using sheet resistance effect of bottom electrode and spin channel effects.