As finger joint method has a high rate of yield and high strength and ease in working, it has been widely used as an end joint method for solid wood and wood based-material. Therefore, we end-joined the material of Pinus densiflora, Quercus variabilis and populus euramericana with polyvinyl acetate adhesive and resorcinol phenol resin adhesive. The effect of difference (0, 0.15, 0.3, 0.45mm) between the dimensions of tip width and root width of the finger (DTRW) on bending strength properties was as follows: 1. In the case of polyvinyl acetate adhesive, DTRW had no effect on bending modulus of elasticity(MOE) and modulus of rupture(MOR) of the three kinds of species, because their bonding layers were destroyed by slippage, not their woody parts. 2. In the case of resorcinol phenol resin adhesive, the material of Quercus variabilis showed an optimal result at 0.15 or 0.3 of DTRW, while the poplar did at 0 of DTRW 3. The differences in efficiency ratio of bending MOR of populus euramericana, Pinus densiflora and Quercus variabilis species according to the kind of adhesive were 13-29%, 23-30% and 45-53%, respectively.