In this paper the ball-on-disk type sliding tests with boundary lubricated steels were carried out to verify the relation between surface profiles and wear as well as scuffing. Three kinds of surface roughness and asperity radius were produced on AISI 1045 steels using the different processes of grinding and polishing. Frictional forces and time to scuffing were measured. Also, the shape and amount of wear particles were analyzed to compare with original profiles. From the tests, it was confirmed that the size of wear particles are very related to original surface profile. The time to failures and wear amounts were sensitive to the surface spacing. The large surface spacing shows much longer sliding life and smaller wear amount than the others. Time to scuffing was increased with increasing surface profile spacing. The sire of wear particles was increased and the amount was decreased with increasing surface profile spacing. Wear volume and wear rate K were decreased with increasing surface profile spacing. And after sliding tests, surface cracks of inner parts of the wear track occurred scuffing were observed and compared the differences about each specimen having the different surface profile spacing.