$Al_2$$O_3$ coatings were deposited on M2 high speed steels by the plasma enhanced chemical vapor deposition (PECVD) process, using a gas mixture of AlC1$_3$, $H_2$, $CO_2$ and Ar $Al_2$$O_3$ coatings had interference color and showed amorphous phase. $A1_2$X$A1_3$/($Ti_{0.5}$ /$Al_{0.5}$ )N double layer coatings were produced in the sequence of substrate $NH_3$ plasma pretreatment, ($Ti_{0.5}$$Al_{0.5}$)N depoition process, $Al_2$$O_3$ deposition process. $Al_2$ $O_3$/( $Ti_{0.5}$A $l_{0.5}$)N double layer coatings showed NaCl structure in ( $Ti_{0.5}$A $l_{0.5}$)N layer and amorphous phase in A1$_2$ $O_3$ layer. It was shown that $Al_2$ $O_3$ columns continuously grew onto ( $Ti_{0.5}$A $l_{0.5}$)N columns. ( $Ti_{0.5}$A $l_{0.5}$)N single coating and $Al_2$ $O_3$/( $Ti_{0.5}$A $l_{0.5}$)N double layer coating were oxidized at $700^{circ}C$, 80$0^{circ}C$, 90$0^{circ}C$ for 1hr, 3hr in atmosphere. At 80$0^{circ}C$, single layer coatings were oxidized, which were examined substrate oxide particle. But $Al_2$ $O_3$/ ( $Ti_{0.5}$A $l_{0.5}$)N double layer coatings maintained the asdeposited state. Therefore, $Al_2$ $O_3$/ ( $Ti_{0.5}$A $l_{0.5}$)N double layer coatings have moreexcellent oxidation resistance than ( $Ti_{0.5}$A $l_{0.5}$)N single layer coatings.X> 0.5/)N single layer coatings.s.