The composition and the microstructure of the lead-tin alloy electrodeposited in a gluconate bath were invesitigated according to electrolysis conditions. The tin content of the lead-tin alloy electrodeposits increased with increasing current density and EDTA addition, while it decreased with increasing temperature and sodium gluconate concentration. The preferred orientation of the alloy deposits changed from the (220) plane through (200) to (200) + (111) planes with increasing cathode overpotential. The surface morphology of the films was closely related to both the preferred orientation and the alloy composition.