The purpose of this study is to determine the effects of Ni on precipitate formation in a Ni added galvanizing bath, which has various Ni content from 0.03wt.% to 0.5wt.%. The addition of hi in the Ni containing galvanizing bath resulted in the formation of Al-Ni intermetallic compounds such as $Al_3$$Ni_2$ and $Al_2$Ni, which make up most of the top precipitates. At 0.07wt.%Ni, Al-Ni intermetallic compound formed sensitively with small amount of Al addition. By analysing the reaction thickness of galvanized steel, it was found that Ni addition in a Zn-0.18w1.%Al bath tended to suppress the formation of Fe-Zn intermetallic compounds but the formation of these compounds increased with increasing Ni concentration above 0.1wt.%.