The possibility of using a glass block with the composition of sodium borosilicate as starting materials for GRIN glass was examined from the view points of the phase separation of the matrix glass, the effects of leaching and the heating conditions for a porous structure, and the change in the refractive index. Glass specimens with similar compositions were prepared in the form of porous glass using a phase-separation technique. An examination of the heating and leaching conditions and the microstructure dependence of these conditions was made.; Specimens with porous structure were obtained when the heat treatment and leaching conditions were fixed at $540^{circ}C$ for 30hrs and in a 0.3N$ H_2$$SO_4$ solution at $100^{circ}C$, respectively. The resultant specimens had some important features on the GRIN glass.; the depth of the gradient and the change in refractive index (Δn) were 4mm and 0.015~0.02, respectively.