Optical investigation on Zn-doped InGaN grown by MOCVD was performed by using the photoluminescence. Two different spectra related to Zn-acceptor-like centers occurred at room temperature, with broad emissions peaking at 2.81, and 2.60 eV, Specially, emissions interacted with phonon were observed at 2.81 eV where phonon energy was 92.5 meV From temperature dependent blue-band emissions of InGaN, we observe that the intensity in high energy region was quickly decreased more than that in low energy region with increased temperature, and the peak position at 2.81 eV was blue shift of about 18 meV, The blue-band emmissions would be originated from the transition related to the localized Zn complex centers.