A new soluble photosensitive poly(amide-co-imide) containing p-phenylenediacryloyl moiety was synthesized and its photoreactivity was characterized. The copolymer was synthesized fromp-phenylenediacryloyl chloride, 4,4-(hexafluoroisopropylidene)diphthalic anhydride and two equivalents of bis(4-aminophenyl) ether in NMP with a subsequent chemical imidization of the resulting poly[amide$xi$ο-(amic acid)] by acetic anhydride and pyridine. The structure and thermal properties of the polymer were characterized by spectroscopic methods and thermal analyses. The polymer was stable up to 350$^{C}$, showed good solubility in polar aprotic solvents, and became insoluble after UV irradiation due to the[2+2] cycloaddition of phenylenediacryloyl moiety. Photoreactivity of the polymer was investigated in solution or as a film with respect to the various exposure conditions by UV/Vis spectroscopy. The photosensitivity was noticeably increased with the irradiation temperature, especially in the presense of photosensitizer. The reason for the increased sensitivity was speculated based on the flexibilization of main chain at elevated temperature. Exposure characteristic curves were obtained from the gel fraction experiments after UV irradiation. The sensitivity and contrast at 160$^{C}$ were measured to be 293 mJ/㎠ and 1.64, respectively.