In this work, thermal decomposition mechanism based on kinetic parameters and thermal stability of carbon fiber-reinforced carbon matrix composites (C/C composites), have been studied under high temperature oxidative conditions with addition of tetra-ethylorthosilicate (TEOS) as an oxidation inhibitor. Thermogravimetric analysis (TGA) was executed to evaluate the thermal decomposition mechanism and thermal stability of C/C composites in the temperature range of 30 ～ $850^{circ}C$. As a result, the kinetic parameters of the composites impregnated with TEOS, i.e., activation energy for thermal decomposition ($E_d$), order of reaction (n) , and pre-exponential factor (A) were evaluated as 136 kJ/mol, 0, and 2.3$ imes$$10^9s^{-1}$, respectively. Especially, the IPDT and $E_d$ of C/C composites impregnated with TEOS were improved largely compared with the composites impregnated without TEOS, due to the formation of $SiO_2$ on composite surfaces, resulting in interrupting the oxygen attack to carbon active site in the composites.