The purpose of this study was to examine the influences of camphoroquinone on the properties of five experimental composites. The contents of camphoroquinone were varied as 0.2%, 0.3%, 0.4%, 0.5%, and 0.6%, with silanized filler 75% and tertiary amine 0.2%. Five kinds of experimental composites were prepared, and diametral tensile strength, shear bond strength, depth of cure and yellowish discoloration were tested as a measurement. Specimen numbers of 10 were applied to all test items and experimental groups. Specimens for testing the diametral tensile strengths with internal diameter of 6mm in diameter and 3mm in height were filled with 5 experimental composites which were crushed with 1mm/min cross-head speed on Instron universal testing machine (Model No. 4467). Shear bond strength was measured on specimens attached to bovine teeth enamel etched with 37% phosphoric acid. Depth of cure was measured by the measurement of height of specimens which were removed the un-polymerized portion with acetone. Yellowness measurements were made by chromometer(Minolta Co. Japan) using L$^*$a$^*$b$^*$ values. ANOVA and Multiple range tests were used analyzed data with confidence level at 95%. The mean value of the shear bond strengths ranged from 31.03MPa to 39.49MPa. Following results were obtained ; 1. Diametral tensile strength was highest in experimental group 3, then was not affected by the contents of camphoroquinone ($r^2$=0.0422). 2. Composite resins containing 0.4% camphoroquinone showed the highest shear bond strength, but there was no statistical significance (p=0.3718). 3. Camphoroquinone reduces the depth of cure in the composite resins (p=0.0004, $r^2$=0.9483). 4. Camphoroquinone made the composites yellowish ($r^2$=0.9815). These results mean that increased content of camphoroquinone reduces the depth of cure, and that camphoroquinone make composites yellowish.