For the purpose of healing the degradation part, $CO_2$ laser beam was irradiated with different irradiation condition (porer, diameter, velocity and beam type) to find out optimum irradiation condition. The test series of hardness, residual stress measurement, and fatigue were carried out after the irradiation. Experimental results show that micro-hardness values on the surface of the irradiated specimens m approximately 2.5 times higher than those of un-irradiated ones. Fatigue tests show that the fatigue life was improved by the compressive residual stress after laser beam irradiation. However, some specimens with different conditions show the shorter fatigue life. It means that laser beam irradiation with optimum irradiation condition and optimum absorb energy, Q can improve the fatigue strength.