Fe-Cr-Al alloy has been studied for application in automobile muffler materials due to good corrosion and oxidation resistance. In order to develop the automobile muffler materials, corrosion behaviors of electron beam physical vapor deposition (EB-PVD) coated surface of muffler matericls of muffler materials were investigated using potentiostat. For 0.1M NaCl solution, corrosion potential and pitting potential of Fe-20Cr-10Al was higher than that of Fe-5Cr- 10Al samples. Especially, in the case of Ti and Nb coated samples, pitting potential increased remarkably compared with non-coated samples. For 0.1M $CaCl_2$ solution, Ti-coated Fe-20Cr-10Al showed remarkably improved pitting corrosion resistance in comparison with non-coated Fe-20Cr-10Al and Fe-5Cr-10Al. The number and size of pits were decreased in the case of Ti coated samples in the 0.1M NaCl and 0.1M $CaCl_2$ solution.