Porous silica-pillared montmorillonites were prepared by simultaneous intercalation of dodecylamine-TEOS [tetraethylorthosilicate, Si(OC2H5)4] into the H-montmorillonite and intragallery amine-catalyzed hydrolysis of TEOS. Mixtures of the H-montmorillonite, dodecylamine and TEOS at molar ratios of 1 : 2 : 15-30 and 1 : 2-6 : 20 resulted to swollen and viscous gel once at room temperature, allowing intercalation compounds which dodecylamine and TEOS were simultaneously intercalated into interlayer of H-montmorillonite. The hydrolysis of the gallery TEOS was conducted in water solution for 40 min at room temperature, affording siloxane-pillared H-montmorillonite. Calcination of samples at 500 $^{circ}C$ in air resulted in silica-pillared montmorillonite with large specific surface areas between 403 and 577 m2 /g, depending on the reaction stoichiometry. The reaction at H-montmorillonite : dodecylamine : TEOS reaction stoichiometries of 1 : 2 : 15 and 1 : 4 : 20 resulted in high specific surface areas and mesopores with a narrow pore size distribution. Result indicates that the intragallery-amine catalyze the hydrolysis of gallery-TEOS and simultaneously have a role of gallery-templated micellar assemblies.