For accurate impression taking, accurate impression material, solid individual tray, and bond strength between impression materials and resin tray are important factors. The purpose of this study was to evaluate tensile bond strength of rubber impression materials to various tray resin materials. This study tested the time dependent tensile bond strength between commercial brands or poly ether, polysulfide, additional silicone impression materials and commercial brands of self curing tray resin. light activited tray resin when applying adhesive Resin specimens were made with 20mm in diameter, 2mm in thickness. 1 made total 360 specimens, 10 per each group and the tensile bond strength was measured by using the Instron($M100EC^{(R)}$, Mecmesin Co., England). The results were as follows ; Comparisons of various impression materials. 1. In case of Impregum $F^{(R)}$, the bond strength of tray resin was decreased in order of SR $Ivolen^{(R)}$, Ostron $100^{(R)}$ Instant tray $mix^{(R)}$, $Lightplast^{(R)}$. All groups excluding Ostron $100^{(R)}$, Instant tray $mix^{(R)}$ are significant difference (p<0.05). Drying time after applying adhesive, the tensile bond strength of tray resin was insignificantly decreased in order of 10 min drying time group. 1 min drying time group. 5 min drying time group. 2. In case of Permlastic $regular^{(R)}$ the bond strength of tray resin was insignificantly decreased in order of Ostron $100^{(R)}$. SR $Ivolen^{(R)}$, Instant tray $mix^{(R)}$ $Lightplast^{(R)}$. About drying time after applying adhesive, the tensile bond strength of tray resin was significantly decreased in order of 5 min drying time group, 10 min drying time group, 1 min drying time group(p<0.05). 3. In case of Exaflex $regular^{(R)}$. the bond strength of tray resin was decreased in order of $Lightplast^{(R)}$, SR $Ivolen^{(R)}$, Instant tray $mix^{(R)}$, Ostron $100^{(R)}$. $Lightplast^{(R)}$ was significant difference(p<0.05). About drying time after applying adhesive, the tensile bond strength of tray resin was decreased in order of 5 min drying time group, 10 min drying time group, 1 min drying time group(p<0.05). Especially 5 min ding time group was significant difference(p<0.05). According to the results of this study, we can see the greatest tensile bond strength when using Impregrm $F^{(R)}$ and Permlastic $regular^{(R)}$ with self curing tray resin, when using Exaflex $regular^{(R)}$ with light activated tray resin In my opinion, adhesive should be dried more than 5 min before impression taking to achieve the greatest tensile bond strength.