For the improvement of denture fitness of changed residual ridge, denture liner can be used. Denture liner should be very stable physically in various environments of the mouth as well as be bonded strongly with denture resin. In this study. the specimens bonded with four kinds of soft denture liner and three kinds of hard denture liner were used to test the physical properties of the liners. All experimental groups were stored in $37{pm}1^{circ}C$ distilled water for 24hours, followed by thermocycling between $15^{circ}C$ and $45^{circ}C$ with 15 second dwell time. 1000, 2000, 3000 cycles of thermocycling were excuted and physical properties were measured by Instron Universal Testing Machine. The obtained results were as follows : 1. In tensile bond test of sea liners, it was shown that both of $Molloplast-B^{(R)}$ specimens before and after thermocycling had the highest tensile strength, and in case of hard liners, Dura-Liner $II^{(R)}$ specimen had the highest tensile strength before and after thermocycling. Depending on thermocycling, $Soft-Relining^{(R)}$, $Denture-Relining^{(R)}$, $Molloplast-B^{(R)}$, $Coe-Soft^{(R)}$ and $Kooliner^{(R)}$ specimen showed significant difference(p<0.05). 2. In strain test of soft liners, it was shown that $Molloplast-B^{(R)}$ specimen before thermocycling and the $Coe-Soft^{(R)}$ after thermocycling showed highest results, and in case of hard liners, the Dura-Liner $II^{(R)}$ specimen before and after thermocycling had the highest result. Depending on thormocycling, $Denture-Relining^{(R)}$, $Molloplast-B^{(R)}$ and Dura-Liner $II^{(R)}$ specimen showed significant difference(p<0.05). 3. In maximum distance test of soft liners. the $Molloplast-B^{(R)}$ specimen before thermocycling and the $Coe-Soft^{(R)}$ after thermocycling showed highest results. and in case of hard liners, the Dura-Liner $II^{(R)}$ specimen before and after thermocycling showed highest result. Depending on thermocycling, $Denture-Relining^{(R)}$, $Molloplast-B^{(R)}$ specimens showed significant difference(p<0.05). 4. In elasticity test of soft liners, the $Molloplast-B^{(R)}$ specimen before and after thermocycling showed highest result. and in case of hard liners, the Dura-Liner $II^{(R)}$ specimen before thermocycling and the $Tokuso-Rebase^{(R)}$ after thermocycling showed highest results. Depending on thermocycling, $Soft-Relining^{(R)}$ $Molloplast-B^{(R)}$ specimens showed significant difference (p<0.05).