The purpose of this study was to compared with the properties of commercial polyvinyl siloxane impression materials on the Korean product and the other country one. The materials used in this study were 5 hydrophilic polvinyly siloxane impression materials of light body automixing type (Perfect-F, Handae Chemical, Korea; Examix, GC, Japan; Contrast, VOCO, Germany; Express, 3M, U.S.A; Extrude, Kerr, U.S.A.). Specimens of each impression material were fabricated from a mold with dimensions identical to that specified in ASTM D624-91 and were subjected to tensile lode at 500 mm/min until failure for tear strength. Properties of consistency, strain in compression, recovery from deformation, detail reproduction and linear dimensional change were tested according to the testing methods of the ISO specification no.4823(1992). From this study, the follow ing results were obtained 1. The tear strength values were high ET(3.4kN/m), EP(3.4kN/m), PF(3.0kN/m), CT(3.0kN/m), but the lowest was EM(2.2kN/m)(p<0.05). 2. In the consistency, CT(47 mm) had the highest value, followed by PF(42.1 mm), ET(41.2 mm), and EM(39.6 mm), EP(39.2 mm)(p<0.05). It means more flow that the consistency value is high. 3. The strain in compression values were high followed by EM(5.8%), PF(52%), CT(4.6%), ET(4.1%), EP(2.9%)(p<0.05). 4. In the recovery from deformation, ET(99.95%) and PF(99.90%) had the highest value, followed by EP(99.75%), EM(99.74%) without statistical signification, CT(99.64%) had the lowest value(p<0.05). 5. Detail reproduction reappeared to line $20{mu}m$ all products. 6. The linear dimensional change was a little shrinked all products. and there were not statistical signification (p>0.05). All products were satisfied the ISO specification.