One of the improtant characteristics of core-shell type nanoparticles is the long-term storage and reuse as an aqueous injection solution when required. For this reason, reconstruction of lyophilized core-shell type nanoparticles is considered to be essential . BAB type triblock copolymers differ from AB type diblock copolymers, which contain the A block as a hydrophilic part and the B block as a hydrophobic part. by not being easily redistributed into phosphate-buffered saline (PBS, pH 7.4, 0.1 M). Therefore, lyophilized core-shell type nanoparticles of CEC triblock copolymer were reconstituted using a somication process with a bar-type sonicator in combination with a freezing-thawing process. Soncation for 30s only resuspended CEC nanoparticles in PBS; their particle size distribution showed a monomodal pattern with narrow size distribution. The bimodal size distribution pattern and the aggregates were reduced by further sonication for 120 s but these nanoparticles showed a wide size distribution. The initial burst of drug release was increased by reconstitution process. The reconstitution of CEC core-shell type nanoparticles by freezing-thawing resulted in trimodal distribution pattern and formed aggregates, although freezing-thawing process was easier than sonication . Drug release form CEC nanoparticles prepared by freezing-thawing was slower than from the original dialysis solution. Although core-shell typenanoparticles of CEC triblock copolymers were not easily performed. Cytotoxicity testing of core-shell type nanoparticles of CEC-2 triblock copolymers containing clonazepam (CNZ) was performed using L929 cells. Cytotoxicity of CNZ was decreased by incorporation into nanoparticles.