To obtain the blue emission of powder electroluminescent device, the emission properties of ZnS:Cu were estimated by the variation of applied frequency and the addition of dye to ZnS:Cu phosphor. The variation of applied frequency was from 400 to 4kHz and the addition ratio of dye was from 0 to 5 weight percent respectively. The increment of applied frequency made that emission peaks were shifted from 500.5nm and 460nm at 400Hz to 490nm and 450nm at 4kHz. CIE coordinate system was shifted from x=0.1647, y=0.3711 at 400Hz to x=0.1543, y=0.1856 at 4kHz. On the basis of applied voltage 100V, 400Hz, the increment of addition ratio of dye also made that emission peak was shifted from 505nm(0wt%) to 490nm(5wt%) and the CIE coordinate system was shifted from x=0.1647, y=0.3711(0wt%) to x=0.1334, y=0.2363 (5wt%). The brightness was increased from 60 cd/$m^2$(400Hz) to 174 cd/$m^2$(4kHz) with increment of frequency. When the addition ratio of dye was above 1wt%, the brightness was decreased below 42% of initial brightness and changed from 60 cd/$m^2$(0wt%) to 20.84 cd/$m^2$(5wt%).