Space charge distributions and behaviors in silane crosslinked polyethylene(SXLPE)/ crosslinked polyethylene(XLPE) laminates were investigated using a pulsed electroacoustic (PEA) method. In case of monolayer, XLPE shows heterocharge while SXLPE shows homocharge. It was observed that charges were accumulated at the interface of SXLPE/XLPE laminate when applied electric field was more than 20kV/mm. The charge profile at various temperatures was also acquired using temperature-controllable PEA system. Although applied electric field is only 8.6 kV.mm, positive interfacial charge starts to appear near 50$^{circ}C$. It was found that the interfacial charge behavior of SXLPE/XLPE laminate under low voltage at high temperature is corresponding to that under high voltage at room temperature.