The effects of the sintering additives such as B $i_2$ $O_3$ and $V_2$ $O_{5}$ on the microwave dielectric and sintering properties of ZnTi $O_3$ system were investigated. Highly dense samples were obtained for ZnTi $O_3$ at the sintering temperature range of 870~90$0^{circ}C$ with B $i_2$ $O_3$ and $V_2$ $O_{5}$ additions of <1 wt.%, respectively. The microwave dielectric properties of ZnTi $O_3$ with 0.6 wt.% B $i_2$ $O_3$ and 0.5 wt.% $V_2$ $O_{5}$ were as follows: Qx $f_{o}$ = 48,400 GHz, $varepsilon$$_{r}$= 22, and $ au$$_{f}$ = -43 ppm/$^{circ}C$. In order to improve temperature coefficient of resonant frequency, Ti $O_2$ was added to the abode system. The optimum amount of Ti $O_2$was 15 mol.% when sintered at 87$0^{circ}C$, at which Ive could obtain following results: Qx $f_{O}$ = 44,700GHz, $varepsilon$$_{r}$ = 26, and $ au$$_{f}$ = 0 PPm/$^{circ}C$.>.EX>.>.>.EX>.>.>.