The SrS:Cu, Ag thin film electroluminescient devices were fabricated on $AlTiO_3$/ITO/glass substrates by electron-beam evaporation. The emission spectrum of the device was about 460 nm with $chi$=0.20, y=0.29 in the CIE color coordinator. It was found that the emission spectrum was saturated to pure blue color when Ag sensitizer was doped in SrS:CuCl phosphors. The luminance of the device was increased by increasing the sulfur pressure. The measured luminance was saturated with 430 cd/$m^2$at the applied voltage of 90 V and the maximum luminance was 580 cd/$m^2$at 110V. The polarization charge and conduction charge of the devices were found to be found to be about $3.5mu$C/$ extrm{cm}^2$ and $7.4mu$C/$ extrm{cm}^2$, respectively.