The Cdl-xZnxTe film was fabricated by thermal evaporation for the flat-panel X-ray detector. The stoichimetric ratio and the crystal structure of a polycrystalline Cd$_{1-x}$ Zn$_{x}$Te were investigated by EPMA and XRD, respectively. The leakage current and X-ray sensitivity of the fabricated films were measured to analyze the X-ray response characteristic of Zn in the polycrystalline CdZnTe thin film. The leakage current and the output charge density of Cd$_{0.7}$Zn$_{0.3}$Te thin film were measured to 0.37 nA/cm$^2$ and 260 pc/cm$^2$ at an applied voltage of 2.5 V/${mu}{ extrm}{m}$, respectively. Experimental results showed that the increase of Zn doping rates in Cd$_{1-x}$ Zn$_{x}$Te detectors reduced the leakage current and improved the signal to noise ratio significantly.antly.tly.