The characteristics of two commercial 2xxx series Al alloy powders, AMB2712 and 201AB, were evaluated and their compacting and sintering characteristics were discussed in tems of compacting pressure. The particle shapes of both two powder mixtures were irregular and their particle size distributions were broad. The compactibility of AMB2712 was superior to that of 201AB because of better fluidity. The sintered density was higher than the green density at low compacting pressure, however, it was lower than the green density when the samples were compacted at higher pressure due to the selling during sintering. The sintered density was alomost the same as the green density at the "homogeneous deformation" stage. It was observed that pores were created at the triple points due to the rapid diffusion of Cu in Al. Cu in Al.