This paper reports on the results of weathering test, tracking test and salt-fog test of various kinds of cycloaliphatic epoxy systems. UV irradiation dramatically induced the loss of surface hydrophobicity due to the chain scission attack at the surface under UV irradiation. It could be seen that samples containing an UV absorbent/antioxidant and a silicone oil additive have a good performance in weathering test, while ATH(alumina tri-hydrate) filled ones have high resistance against tracking failure than others. Under salt fog chamber test, specimens mixed with silicone oil are able to suppress leakage current development. It was thought that silicone oil mixed into cycloaliphatic epoxy system could lead to lower the surface energy and to retain hydrophobic properties for a long time, which are desirable for outdoor use