In order to make the high purity Mn$_3$O$_4$powder for the raw material of soft ferrite, Mn is extracted from the dust and the extracted solution is refined. The dust is generated in producing a medium-low carbon ferromanganese and contains 90% Mn$_3$O$_4$. Mn$_3$O$_4$in the dust was reduced into MnO by roasting with charcoal. Injection of the 180g/L of the reduced dust into 4N HCI solution increased pH of the leaching solution higher than 5 and then a ferric hydroxide was precipitated. Because the ferric hydroxide co-precipitates with Si ion etc, Fe and Si ion was removed from the solution and the about 10% Mn solution was obtained. The solution was diluted with water to Mn-15000 ppm and $NH_4$F was injected into the diluted solution at $70^{circ}C$ to the F-3000 ppm. As a result, Ca ion is precipitated as $CaF_2$and the residual concentration of Ca was 14 ppm. Injection of the equivalent (NH$1.5M_4$)$_2$$CO_3$solution as 2 L/min at $25^{circ}C$ into the above solution precipitated a fine and high purity $MnCO_3$powder. The deposition was filtrated and roasted at $1000^{circ}C$ for 2 hours. As a result, $MnCO_3$powder is converted into $Mn_3$$O_4$powder and it had $8.2mu$m of median size. The final production is above 99% $Mn_3$$O_4$powder and it satisfied the requirement of high purity $Mn_3$$O_4$powder for a raw material of soft ferrite.