Piezoelectric properties of PZT-PSN ceramics were investigated as a function of WO$_3$ addition from 0 wt% to 6.0 wt%. The dielectric and piezoelectric characteristics of PZT-PSN ceramics have been investigated at different calcination (80$0^{circ}C$~90$0^{circ}C$) and sintering (110$0^{circ}C$~130$0^{circ}C$) temperatures. The grain size was increased with the addition of WO$_3$and the sintering temperatures. Anisotropic properties of electromechanical coupling coefficient and piezoelectric coefficient are proven to be dependent on processing temperatures and amount of addition. At the specimen with 0.6 wt% WO$_3$ addition, using calcination temperature of 80$0^{circ}C$ and sintering temperature of 110$0^{circ}C$ , mechanical quality factor(Q$_{m}$) and electromechanical coupling coefficient(k$_{p}$) showed the excellent results of 1560 and 0.48, respectively Experimental results indicated that the PZT-PSN system ceramics with WO$_3$impurity could be effectively used for the microtransformer and actuator applications, etc.etc.