Metal matrix composites had generated a lot of interest in recent times because of significant in specific properties, it was also highlighted as the material of frontier industry because strength, heat-resistant, corrosion-resistant and wear-resistant were superiored. In recent years, the study of metal matrix composite has increased by aluminum alloy. The study is based on the tribological properties of AC4CH that is a part of the mechanical property of metal matrix composites. Metal matrix composite that is produced from matrix material AC4CH and reinforcement SiO$_2$, Al$_2$O$_3$ and TiO$_2$ are added to the metal matrix composite fur strength so binding among the whisker can take place. Each metal matrix composite is produced using the squeeze casting method. To test for tribe a pin-on-disk machine and lubricant is used without paraffine 8.2CST at room temperature which is 40$^{C}$. As the results of this study, the tribological properties of each specimen are more improved than AC4CH. The variation of coefficient resistance is more stable at the AC4CH and TiO$_2$, but the variation rates are higher at the inanimate binder.