The effects of boron or manganese added as $B_4C$, Mn, $TiB_2$, B on TiC-30vo1.%$Ni_3Al$ cermet sintered at 1380 and $1400^{circ}C$ for 1 hour, were examined in relation with shrinkage, relative density, microstructure, lattice parameter, hardness and fracture toughness ($K_{IC}$). The results are summarized as follows: 1) The highest shrink-age showed about 30.5% in the specimen added B$_4$C and the maximum relative density was about 99% in the specimen added $TiB_2$; 2) The grains of TiC were grown during sintering and made the surrounding structure by adding boron and manganese. The largest grain size showed about $2.8mutextrm{m}$ in the specimen with boron sintered at $1400^{circ}C$;3) The lattice parameter of TiC was about $4.325AA$ and $Ni_3Al$ about $3.592AA$ by adding other elements; 4) The highest hardness was about $1100kgf/ extrm{mm}^2$ in the specimen with B4C; 5) The fracture toughness ($K_{IC}$) showed about $15MNm^{-3/2}$ in the specimen added $TiB_2$.