The $CaTio_3$powder with perovskite structure was synthesized by mixing anatase $TiO_2$and $Ca(OH)_2$powders as starting materials, and KOH or NaOH as mineralizer, followed by hydrothermal method. The change of crystal structure, particle shape and size of the synthesized $CaTiO_3$powder was investigated with kind and concentration of mineralizer. It was found that the spherical particles of 0.7 $mu$m were obtained when using 1N KOH and the hexahedrons particles of 3$mu$m were obtained for the case of using 10 N KOH. With increasing KOH concentration, the particle shape was changed from sphere to hexahedrons and its size also increased. When using 1 N NaOH, the powder was consisted of 0.5~1 $mu$m particle in size, whereas hexahedrons of 1~4 $mu$m and whiskers more than 10$mu$m in size was obtained for the 10 N NaOH solution. With increasing NaOH concentration, the particle shape was varied from hexahedrons to whiskers, showing the similar result with the KOH case. It was confirmed from EDS analysis that Na element, which was detected in hexahedrones was not contained in the whiskers.