Band gap tuning by quantum well disordering in $In_{0.53}Ga_{0.47}As/InGaAsP(Q1.25)$ quantum well structure has been investigated using photoluminescence. The threshold temperature for the blue shift was about $750^{circ}C$ , and the blue shift became larger as the annealing temperature increased. $SiO_2$ showed saturation as the annealing temperature increased. $SiN_x$caused larger blue shift than $SiO_2$, which is considered to be related to the low growth temperature of $SiN_x$. The diffusion of P and Ga are thought to be responsible for the blue shift of the $SiN_x$ and $SiO_2$capped quantum well disordering , respectively.