Metal-ferroelectric-semiconductor(MFS) capacitors by using rapid thermal annealed $LiNbO_3$/Si structures were successfully fabricated and demonstrated nonvolatile memory operations of the MFS capacitors. The C-V characteristics of MFS capacitors showed a hysteresis loop due to the ferroelectric nature of the $LiNbO_3$thin film. The dielectric constant of the $LiNbO_3$film calculated from the capacitance in the accumulation region in the capacitance-voltage(C-V) curve was about 25. The gate leakage current density of MFS capacitor using a platinum electrode showed the least value of $1{ imes}10^{-8} extrm{A/cm}^2$ order at the electric field of 500 kV/cm. The minimum interface trap density around midgap was estimated to be about $10^{11}/cm^2$.eV. The typical measured remnant polarization(2Pr) value was about 1.2 $mu extrm{C/cm}^2$, in an applied electric field of $pm$ 300 kv/cm. The ferroelectric capacitors showed no polarization degradation up to about $10^{10}$ switching cycles when subjected to symmetric bipolar voltage pulse in the 500 kHz.