The purpose of this study was to compare microleakage and marginal hybrid layer in class V restorations using two one-bottle adhesives and one self-etching adhesive. Class V cavity preparations with occlusal margins in enamel and gingival margins in dentin were pre-pared on buccal and lingual surfaces of 30 extracted human molar teeth. Prepared teeth were randomly divided into three treatment groups (n=30) and restored with three adhesives and composites: Single Bond/Filtek Z-250 (Group 1), Prime&BondNT/Esthet.X (Group 2), UniFil Bond/UniFil F (Group 3). For microleakage, samples were stored in room temperature water for 24 hours, thermocycled stained with 2% methylene blue dye, sectioned into halves, scored and analysed using Mann-whitney test and Wilcoxon signed rank sum test. For marginal hybrid layer, samples were sectioned into halves, treated with 10% phosphoric acid for 5 seconds, stored in 5% NaOCL solution for 24 hours, dried and gold coated. Occlusal and gingival margins of each sample were inspected under SEM. The results of this study were as follows ; 1. Microleakage at the occlusal margins was not evident in group 1 and group 2, but it showed in group 3 (p<0.05). 2. Microleakage in group 1 and group 3 was significantly lower than in group 2 at gingival margins (p<0.05). 3. Microleakage at gingival margins was greater than at occlusal margins in group 1 and group 2, but microleakage at occlusal margins was greater than at gingival margins in group 3 (p<0.05). 4. In group 1 and group 2, no gaps at occlusal margins showed. But gaps showed in group 3. Occlusal margins were free from a hybrid layer in all groups 5. The thickness of the marginal hybrid layers was 2.5~5 $mu extrm{m}$ thick in group 5 $mu extrm{m}$ thick in group 2 and 1.5 $mu extrm{m}$ thick in group 3. 6 There was no corelation between microleakage and thickness of marginal hybrid layer. In coclusion, the effect of dentin adhesives on microleakge in class V composite restorations was excellent when one-bottle adhesives were applied on enamel margin, and it was good when a self-etching adhesive was applied on dentinal margin. There was no corelation between microleakage and thickness of marginal hybrid layer.