The resistance curves (R-curves) for 381 m crack extension of CLWL-DCB specimens had been determined. The average velocities of the crack extension measured with strain gages were 0.70 and 55 ㎜/sec. The measured rotation angle of the notch faces showed the existence of the singularity at least before 171 and 93 mm crack extensions for the 0.70 and 55 ㎜/sec crack velocities, respectively. The maximum slopes of the R-curves occurred between 25 and 89 ㎜ crack extensions for 0.70 ㎜/sec crack velocity and between 51 and 127 ㎜ crack extensions for 55 ㎜/sec crack velocity During the maximum slopes of the R-curves, the micro-crack localization can be expected, and faster crack velocity may form longer micro-cracking and micro-crack localizing zones. The fracture resistance of 0.70 ㎜/sec crack velocity reached a roughly constant maximum value of 143 N/m at 152 ㎜ crack extension, while that of 55 ㎜/sec crack velocity increased continuously to 245 N/m at 254 ㎜ crack extension and then decreased to the value of 0.70 ㎜/sec crack velocity. The R-curve of 55 ㎜/sec crack velocity was similar to that of the small size three-point bend test, and it showed that small size specimen or fast crack velocity could cause more brittle behavior.