This study investigated the effect of temporary cement and desensitizer on the bond strength of luting cements. Total 96 dentin specimens were divided into two groups with and without temporary cementation. For temporary cement-tread group, specimens were cemented with $Temp-bond^{(R)}$ and all specimens were stored in distilled water at $37^{circ}C$ for 7 days. Each cup was further divided into 3 subgroups with $Gluma^{(R)},;One-step^{(R)}$ application and without desensitizer After desensitizer application, Ni-Cr specimens were luted to dentin surface with $Panavia-F^{(R)}$ and $Vitremer^{(R)}$ Specimens were placed in distilled water at $37^{circ}C$ for 24 hours and shear bond strength between metal and dentin was measured by a universal testing machine. The results were as follows : 1. In $Panavia-F^{(R)}$ cemented groups, the combination of $One-step^{(R)}$ without temporary cement showed the greatest strength. Among the desensitizer types, $One-step^{(R)}$ showed the highest bond strength, followed by No-desensitizer, $Gluma^{(R)}$. 2. In $Vitremer^{(R)}$ cemented groups, the combination of no temporary cement and without desensitizer showed the greatest bond strength. Among the desensitizer types, No-desensitizer group showed the highest bond strength. 3. The use of $Gluma^{(R)}$ significantly reduced the shear bond strength in $Panavia-F^{(R)}$ and $Vitremer^{(R)}$ groups. 4. All temporary cement-treated groups showed a significant lower shear bond strength than without temporary cement groups. 5. Desensitizer application significantly influenced the bond strength of the resin cement and resin modified glass ionomer cement.