Vanadium oxides supported on zirconia and modified with MoO₃were prepared by adding Zr(OH)₄powder into a mixed aqueous solution of ammonium metavanadate and ammonium molybdate followed by drying and calcining at high temperatures. The characterization of prepared catalysts was performed using FTIR, Raman spectroscopy and solid-state $^{51}V$ NMR. In the case of a calcination temperature of 773 K, for samples containing low loading of $V_2O_5$, below 15 wt %, vanadium oxide was in a highly dispersed state, while for samples containing high loading of $V_2O_5$, equal to or above 15 wt %, vanadium oxide was well crystallized because the $V_2O_5$ loading exceeded the formation of a monolayer on the surface of $ZrO_2$. The $ZrV_2O_7$ compound was formed through the reaction of $V_2O_5;and;ZrO_2$ at 873 K and the compound decomposed into $V_2O_5;and;ZrO_2$ at 1073 K, which were confirmed by FTIR spectroscopy and solid-state $^{51}V$ NMR. IR spectroscopic studies of ammonia adsorbed on $V_2O_5-MoO_3/ZrO_2$ showed the presence of both Lewis and Bronsted acids.