Removal of gas in a mold has been a big problem in pressing mold or in injection mold. Air vent has been used to solve the problem, but it has weak points such as the increased cost, the increased number of process, and vent marks on the surface of a product. In this study, the sintering method and rapid tooling method are used for making porous metal mold. Porous metal mold has many open pores, which are very small. When porous metal mold is used for pressing mold or injection mold, all process would be made short, produce cost would be down, and vent marks would be not leaved on the surface of a product. Characteristic of porous material varies from sintering conditions, which are the length of sintering time, sintering temperature and sintering atmosphere etc. This study will find optimized sintering condition for the porous metal mold.