Etching species in CF$_4$/Ar plasma and the behavior of etching rate of Bi$_4$-$_{x}$L$_{x}$rTi$_3$O$_2$ (BLT) films were investigated in inductively coupled plasma (ICP) reactor in terms of etch parameters. The etching rate as functions of CF$_4$ contents showed the maximum 803 $AA$/min at 20% CF$_4$ addition in CF$_4$/Ar plasma. The increase of RF power and DC bias voltage caused to an increase of etch rate. The variation of relative volume densities for F and he atoms were measured with the optical emission spectroscopy (OES). The chemical states of BLT were investigated with using X-ray photoelectron spectroscopy (XPS). XPS narrow scan analysis shows that La-fluorides remained on the etched surface. The presence of maximum etch rate at CF$_4$(20%)/Ar(80%) may be explained by the concurrence of two etching mechanisms such as physical sputtering and chemical reaction. The roles of he ion bombardment include destruction of metal (Bi, La, Ti)-O bonds as well as assistant for chemical reaction of metals with fluorine atoms.oms.